• Model Number: AP-589
• Place of Origin: Guangdong, China
• Minimum Order Quantity: 0 Pieces
• Supply Capacity: 0 Pieces/month
• MemberShip: Free Member
• Inquiry Now
• Bookmark & Share:

Description

1.General:

AP-589 is the double component Si-H addition reaction, solidifies the high performance gel; After curing, the gelatin has the outstanding electrical specification, ageing-resistant, excellent freeze and heat durability (- 40~150) ¡æ, waterproof and dampproof, viscousness, in-depth solidifies, and also It does not have the corrosive action to the cementation material and never pollute the environment; Conforms to the RoHS instruction and the related environmental protection request.


2. Technical Parameter





NO.



Test Item



Technical parameters





Be same as 599¢ó





1



Before cured(A component)



Appearance



black, white liquid





2



Viscosity(mPa.s)



2500--4000





3



After cured(B component)



Appearance



Clear liquid





4



Viscosity(mPa.s)



2500--4000





5



Mix ratio(A©sB)



1©s1(volume ratio or weight ratio)





6



After cured



Appearance



white, black, liquid gel





7



Operation time in room tempreture(min)



≥30





8



Curing time in room tempreture(hour)



¨Q24





9



80¡æ curing time(min)



≤30





10



Penetration (mm/10)



200-230





11



Compressive strength (kv/mm)



£¾25





12



Volume resistivity (Ω·cm)



1.0×1014





Note: Above data for room temperature environment test.



3.Application:

Apply to the solar energy, the sensor as well as the automobile, the power converter module and opto-electronic equipment's electronic component, the integrated circuit and the feed line box seal waterproofing, the moisture-proof protection.


4.Usage:

1. Measure: accurate weighing A, B component;

2. Mixes the silicon gel: Join B component to A component and then uniform mixing;

3. Deaeration: to put the sizing material in the vacuum cabinet the deaeration;

4. Pouring: fills the sizing material seals in the spare part; (Before filling seals, in order to avoid influence solidification, pls keep the components surface and mixer clean and dry, cannot contact chemical compound such as N, P, S, Sn, Pb, Hg and so on.)

5. Solidification: Curing the components by room temperature or heating.



5. Announcements:

Certain material©pchemical agent©pcuring agent and the plasticizer may suppress gel’s solidification; Should pay attention materials: the organic tin and containing organic tin; the sulfur©ppolysulfide or containing sulfur ; The amine©ppolyurethane rubber or containing ammonia; the phosphorus or containing phosphorus; acidic (organic acid) and some flux residues; If suspicion includes the above material before the use, we suggested makes the sample test confirmation after first, then volume production.



6.Packing and storage

Packing: 16kg/sets (A component 8kg + B component 8kg), or according to the customer's requirements, This product is nontoxic non-dangerous cargo, please transport as general chemical, and preserve in shade and keep it dry. The preserve period is 12months.